S44725 Stainless Steel vs. EN 1.0644 Steel

Both S44725 stainless steel and EN 1.0644 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S44725 stainless steel and the bottom bar is EN 1.0644 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 22
17
Fatigue Strength, MPa 210
380
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 320
420
Tensile Strength: Ultimate (UTS), MPa 500
690
Tensile Strength: Yield (Proof), MPa 310
570

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
47
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.4
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.8
Embodied Energy, MJ/kg 44
24
Embodied Water, L/kg 170
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
110
Resilience: Unit (Modulus of Resilience), kJ/m3 240
870
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 4.6
13
Thermal Shock Resistance, points 16
22

Alloy Composition

Aluminum (Al), % 0
0.010 to 0.050
Carbon (C), % 0 to 0.015
0.16 to 0.22
Chromium (Cr), % 25 to 28.5
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 67.6 to 73.5
96.1 to 98.4
Manganese (Mn), % 0 to 0.4
1.3 to 1.7
Molybdenum (Mo), % 1.5 to 2.5
0 to 0.080
Nickel (Ni), % 0 to 0.3
0 to 0.4
Niobium (Nb), % 0 to 0.26
0 to 0.070
Nitrogen (N), % 0 to 0.018
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 0.040
0.1 to 0.5
Sulfur (S), % 0 to 0.020
0 to 0.035
Titanium (Ti), % 0 to 0.26
0 to 0.050
Vanadium (V), % 0
0.080 to 0.15