MakeItFrom.com
Menu (ESC)

S44725 Stainless Steel vs. EN 1.4971 Stainless Steel

Both S44725 stainless steel and EN 1.4971 stainless steel are iron alloys. They have 54% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S44725 stainless steel and the bottom bar is EN 1.4971 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
240
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 22
34
Fatigue Strength, MPa 210
270
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
81
Shear Strength, MPa 320
530
Tensile Strength: Ultimate (UTS), MPa 500
800
Tensile Strength: Yield (Proof), MPa 310
340

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 500
570
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 17
13
Thermal Expansion, µm/m-K 11
15

Otherwise Unclassified Properties

Base Metal Price, % relative 15
70
Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 3.1
7.6
Embodied Energy, MJ/kg 44
110
Embodied Water, L/kg 170
300

Common Calculations

PREN (Pitting Resistance) 33
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
220
Resilience: Unit (Modulus of Resilience), kJ/m3 240
280
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
26
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 4.6
3.4
Thermal Shock Resistance, points 16
19

Alloy Composition

Carbon (C), % 0 to 0.015
0.080 to 0.16
Chromium (Cr), % 25 to 28.5
20 to 22.5
Cobalt (Co), % 0
18.5 to 21
Iron (Fe), % 67.6 to 73.5
24.3 to 37.1
Manganese (Mn), % 0 to 0.4
0 to 2.0
Molybdenum (Mo), % 1.5 to 2.5
2.5 to 3.5
Nickel (Ni), % 0 to 0.3
19 to 21
Niobium (Nb), % 0 to 0.26
0.75 to 1.3
Nitrogen (N), % 0 to 0.018
0.1 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.040
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0 to 0.26
0
Tungsten (W), % 0
2.0 to 3.0