S44725 Stainless Steel vs. EN 1.5402 Steel

Both S44725 stainless steel and EN 1.5402 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S44725 stainless steel and the bottom bar is EN 1.5402 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 22
23
Fatigue Strength, MPa 210
260
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 320
370
Tensile Strength: Ultimate (UTS), MPa 500
580
Tensile Strength: Yield (Proof), MPa 310
370

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
51
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.4
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.7
Embodied Energy, MJ/kg 44
22
Embodied Water, L/kg 170
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
120
Resilience: Unit (Modulus of Resilience), kJ/m3 240
360
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 4.6
14
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0 to 0.015
0 to 0.18
Chromium (Cr), % 25 to 28.5
0
Iron (Fe), % 67.6 to 73.5
97.3 to 98.7
Manganese (Mn), % 0 to 0.4
0.9 to 1.4
Molybdenum (Mo), % 1.5 to 2.5
0.4 to 0.6
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.26
0
Nitrogen (N), % 0 to 0.018
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.040
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0 to 0.26
0
Vanadium (V), % 0
0.040 to 0.080