S45000 Stainless Steel vs. S38815 Stainless Steel
Both S45000 stainless steel and S38815 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is S45000 stainless steel and the bottom bar is S38815 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 280 to 410 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 6.8 to 14 | |
| 34 |
| Fatigue Strength, MPa | 330 to 650 | |
| 230 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 74 |
| Shear Strength, MPa | 590 to 830 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 980 to 1410 | |
| 610 |
| Tensile Strength: Yield (Proof), MPa | 580 to 1310 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 370 |
| Maximum Temperature: Corrosion, °C | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 840 | |
| 860 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1360 |
| Melting Onset (Solidus), °C | 1390 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 500 |
| Thermal Expansion, µm/m-K | 11 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 19 |
| Density, g/cm3 | 7.8 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.8 |
| Embodied Energy, MJ/kg | 39 | |
| 54 |
| Embodied Water, L/kg | 130 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 17 | |
| 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 to 160 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 850 to 4400 | |
| 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 35 to 50 | |
| 22 |
| Strength to Weight: Bending, points | 28 to 36 | |
| 21 |
| Thermal Shock Resistance, points | 33 to 47 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.3 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.030 |
| Chromium (Cr), % | 14 to 16 | |
| 13 to 15 |
| Copper (Cu), % | 1.3 to 1.8 | |
| 0.75 to 1.5 |
| Iron (Fe), % | 72.1 to 79.3 | |
| 56.1 to 67 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.5 to 1.0 | |
| 0.75 to 1.5 |
| Nickel (Ni), % | 5.0 to 7.0 | |
| 13 to 17 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 5.5 to 6.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |