S45503 Stainless Steel vs. N06985 Nickel
S45503 stainless steel belongs to the iron alloys classification, while N06985 nickel belongs to the nickel alloys. They have 43% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is S45503 stainless steel and the bottom bar is N06985 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 4.6 to 6.8 | |
| 45 |
| Fatigue Strength, MPa | 710 to 800 | |
| 220 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 80 |
| Shear Strength, MPa | 940 to 1070 | |
| 480 |
| Tensile Strength: Ultimate (UTS), MPa | 1610 to 1850 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 1430 to 1700 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 990 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1350 |
| Melting Onset (Solidus), °C | 1400 | |
| 1260 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 11 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 55 |
| Density, g/cm3 | 7.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 8.8 |
| Embodied Energy, MJ/kg | 48 | |
| 120 |
| Embodied Water, L/kg | 120 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 to 110 | |
| 250 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 57 to 65 | |
| 23 |
| Strength to Weight: Bending, points | 39 to 43 | |
| 21 |
| Thermal Shock Resistance, points | 56 to 64 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.015 |
| Chromium (Cr), % | 11 to 12.5 | |
| 21 to 23.5 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Copper (Cu), % | 1.5 to 2.5 | |
| 1.5 to 2.5 |
| Iron (Fe), % | 72.4 to 78.9 | |
| 18 to 21 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 6.0 to 8.0 |
| Nickel (Ni), % | 7.5 to 9.5 | |
| 35.9 to 53.5 |
| Niobium (Nb), % | 0.1 to 0.5 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 1.0 to 1.4 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0 to 1.5 |