S46500 Stainless Steel vs. ASTM B817 Type I
S46500 stainless steel belongs to the iron alloys classification, while ASTM B817 type I belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is S46500 stainless steel and the bottom bar is ASTM B817 type I.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 2.3 to 14 | |
| 4.0 to 13 |
| Fatigue Strength, MPa | 550 to 890 | |
| 360 to 520 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 75 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 1260 to 1930 | |
| 770 to 960 |
| Tensile Strength: Yield (Proof), MPa | 1120 to 1810 | |
| 700 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 780 | |
| 340 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1600 |
| Melting Onset (Solidus), °C | 1410 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 560 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 36 |
| Density, g/cm3 | 7.9 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 38 |
| Embodied Energy, MJ/kg | 51 | |
| 610 |
| Embodied Water, L/kg | 120 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 210 | |
| 30 to 120 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 44 to 68 | |
| 48 to 60 |
| Strength to Weight: Bending, points | 33 to 44 | |
| 42 to 49 |
| Thermal Shock Resistance, points | 44 to 67 | |
| 54 to 68 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 to 0.020 | |
| 0 to 0.1 |
| Chlorine (Cl), % | 0 | |
| 0 to 0.2 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 72.6 to 76.1 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0 to 0.25 | |
| 0 |
| Molybdenum (Mo), % | 0.75 to 1.3 | |
| 0 |
| Nickel (Ni), % | 10.7 to 11.3 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 to 0.1 |
| Sodium (Na), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 1.5 to 1.8 | |
| 87 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |