S46500 Stainless Steel vs. Nickel 200
S46500 stainless steel belongs to the iron alloys classification, while nickel 200 belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is S46500 stainless steel and the bottom bar is nickel 200.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 180 |
| Elongation at Break, % | 2.3 to 14 | |
| 23 to 44 |
| Fatigue Strength, MPa | 550 to 890 | |
| 120 to 350 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 75 | |
| 70 |
| Shear Strength, MPa | 730 to 1120 | |
| 300 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 1260 to 1930 | |
| 420 to 540 |
| Tensile Strength: Yield (Proof), MPa | 1120 to 1810 | |
| 120 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 780 | |
| 900 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 65 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 11 |
| Embodied Energy, MJ/kg | 51 | |
| 150 |
| Embodied Water, L/kg | 120 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 210 | |
| 110 to 150 |
| Stiffness to Weight: Axial, points | 14 | |
| 11 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 44 to 68 | |
| 13 to 17 |
| Strength to Weight: Bending, points | 33 to 44 | |
| 14 to 17 |
| Thermal Shock Resistance, points | 44 to 67 | |
| 13 to 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0 to 0.15 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 72.6 to 76.1 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0 to 0.25 | |
| 0 to 0.35 |
| Molybdenum (Mo), % | 0.75 to 1.3 | |
| 0 |
| Nickel (Ni), % | 10.7 to 11.3 | |
| 99 to 100 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.010 |
| Titanium (Ti), % | 1.5 to 1.8 | |
| 0 |