S46800 Stainless Steel vs. ASTM Grade LCC Steel

Both S46800 stainless steel and ASTM grade LCC steel are iron alloys. They have 80% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S46800 stainless steel and the bottom bar is ASTM grade LCC steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
25
Fatigue Strength, MPa 160
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 470
570
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 920
400
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 23
49
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 37
18
Embodied Water, L/kg 130
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
120
Resilience: Unit (Modulus of Resilience), kJ/m3 130
260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 6.1
13
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.25
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 76.5 to 81.8
96.9 to 100
Manganese (Mn), % 0 to 1.0
0 to 1.2
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0.1 to 0.6
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.045
Titanium (Ti), % 0.070 to 0.3
0
Residuals, % 0
0 to 1.0