S46800 Stainless Steel vs. N08926 Stainless Steel

Both S46800 stainless steel and N08926 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S46800 stainless steel and the bottom bar is N08926 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
40
Fatigue Strength, MPa 160
290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
80
Shear Strength, MPa 300
500
Tensile Strength: Ultimate (UTS), MPa 470
740
Tensile Strength: Yield (Proof), MPa 230
330

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 500
420
Maximum Temperature: Mechanical, °C 920
1100
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 23
12
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.6
6.2
Embodied Energy, MJ/kg 37
84
Embodied Water, L/kg 130
200

Common Calculations

PREN (Pitting Resistance) 19
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
240
Resilience: Unit (Modulus of Resilience), kJ/m3 130
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
25
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 6.1
3.2
Thermal Shock Resistance, points 16
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 18 to 20
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 76.5 to 81.8
41.7 to 50.4
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0 to 0.5
24 to 26
Niobium (Nb), % 0.1 to 0.6
0
Nitrogen (N), % 0 to 0.030
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0.070 to 0.3
0