S64512 Stainless Steel vs. SAE-AISI 8622 Steel

Both S64512 stainless steel and SAE-AISI 8622 steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is SAE-AISI 8622 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
26
Fatigue Strength, MPa 540
240
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 700
320
Tensile Strength: Ultimate (UTS), MPa 1140
500
Tensile Strength: Yield (Proof), MPa 890
330

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
38
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.5
Embodied Energy, MJ/kg 47
20
Embodied Water, L/kg 110
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
280
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
18
Strength to Weight: Bending, points 31
18
Thermal Diffusivity, mm2/s 7.5
10
Thermal Shock Resistance, points 42
17

Alloy Composition

Carbon (C), % 0.080 to 0.15
0.2 to 0.25
Chromium (Cr), % 11 to 12.5
0.4 to 0.6
Iron (Fe), % 80.6 to 84.7
96.9 to 98
Manganese (Mn), % 0.5 to 0.9
0.7 to 0.9
Molybdenum (Mo), % 1.5 to 2.0
0.15 to 0.25
Nickel (Ni), % 2.0 to 3.0
0.4 to 0.7
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.040
Vanadium (V), % 0.25 to 0.4
0