S66286 Stainless Steel vs. AISI 440C Stainless Steel
Both S66286 stainless steel and AISI 440C stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is S66286 stainless steel and the bottom bar is AISI 440C stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 17 to 40 | |
| 2.0 to 14 |
| Fatigue Strength, MPa | 240 to 410 | |
| 260 to 840 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 76 |
| Shear Strength, MPa | 420 to 630 | |
| 430 to 1120 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1020 | |
| 710 to 1970 |
| Tensile Strength: Yield (Proof), MPa | 280 to 670 | |
| 450 to 1900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 780 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 870 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1480 |
| Melting Onset (Solidus), °C | 1370 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 22 |
| Thermal Expansion, µm/m-K | 17 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.2 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 9.0 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 2.2 |
| Embodied Energy, MJ/kg | 87 | |
| 31 |
| Embodied Water, L/kg | 170 | |
| 120 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 200 | |
| 39 to 88 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 36 | |
| 26 to 71 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 23 to 46 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 6.0 |
| Thermal Shock Resistance, points | 13 to 22 | |
| 26 to 71 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0 |
| Boron (B), % | 0.0010 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 1.0 to 1.2 |
| Chromium (Cr), % | 13.5 to 16 | |
| 16 to 18 |
| Iron (Fe), % | 49.1 to 59.5 | |
| 78 to 83.1 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 1.0 to 1.5 | |
| 0 to 0.75 |
| Nickel (Ni), % | 24 to 27 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 1.9 to 2.4 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.5 | |
| 0 |