S82011 Stainless Steel vs. EN 1.4307 Stainless Steel

Both S82011 stainless steel and EN 1.4307 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S82011 stainless steel and the bottom bar is EN 1.4307 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
180 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
14 to 46
Fatigue Strength, MPa 410
190 to 320
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 490
410 to 550
Tensile Strength: Ultimate (UTS), MPa 730
590 to 900
Tensile Strength: Yield (Proof), MPa 510
200 to 570

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 1010
940
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
3.0
Embodied Energy, MJ/kg 37
43
Embodied Water, L/kg 150
140

Common Calculations

PREN (Pitting Resistance) 27
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 660
100 to 810
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
21 to 32
Strength to Weight: Bending, points 24
20 to 27
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 20
13 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 20.5 to 23.5
17.5 to 19.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 68.6 to 76.3
66.8 to 74.5
Manganese (Mn), % 2.0 to 3.0
0 to 2.0
Molybdenum (Mo), % 0.1 to 1.0
0
Nickel (Ni), % 1.0 to 2.0
8.0 to 10.5
Nitrogen (N), % 0.15 to 0.27
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015