S82031 Stainless Steel vs. ACI-ASTM CA6N Steel

Both S82031 stainless steel and ACI-ASTM CA6N steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S82031 stainless steel and the bottom bar is ACI-ASTM CA6N steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
17
Fatigue Strength, MPa 490
640
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 780
1080
Tensile Strength: Yield (Proof), MPa 570
1060

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 430
390
Maximum Temperature: Mechanical, °C 980
740
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
23
Thermal Expansion, µm/m-K 13
9.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 13
11
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
2.5
Embodied Energy, MJ/kg 39
35
Embodied Water, L/kg 150
110

Common Calculations

PREN (Pitting Resistance) 27
12
Resilience: Ultimate (Unit Rupture Work), MJ/m3 280
180
Resilience: Unit (Modulus of Resilience), kJ/m3 820
2900
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
38
Strength to Weight: Bending, points 24
30
Thermal Diffusivity, mm2/s 3.9
6.1
Thermal Shock Resistance, points 22
40

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.060
Chromium (Cr), % 19 to 22
10.5 to 12.5
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 68 to 78.3
77.9 to 83.5
Manganese (Mn), % 0 to 2.5
0 to 0.5
Molybdenum (Mo), % 0.6 to 1.4
0
Nickel (Ni), % 2.0 to 4.0
6.0 to 8.0
Nitrogen (N), % 0.14 to 0.24
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.020