S82031 Stainless Steel vs. ASTM A182 Grade FR

Both S82031 stainless steel and ASTM A182 grade FR are iron alloys. Both are furnished in the annealed condition. They have 76% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S82031 stainless steel and the bottom bar is ASTM A182 grade FR.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
28
Fatigue Strength, MPa 490
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
72
Shear Strength, MPa 540
320
Tensile Strength: Ultimate (UTS), MPa 780
490
Tensile Strength: Yield (Proof), MPa 570
360

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 980
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 13
3.3
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.8
1.6
Embodied Energy, MJ/kg 39
21
Embodied Water, L/kg 150
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 280
120
Resilience: Unit (Modulus of Resilience), kJ/m3 820
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
17
Strength to Weight: Bending, points 24
17
Thermal Diffusivity, mm2/s 3.9
14
Thermal Shock Resistance, points 22
14

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.2
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0 to 1.0
0.75 to 1.3
Iron (Fe), % 68 to 78.3
95.2 to 97.3
Manganese (Mn), % 0 to 2.5
0.4 to 1.1
Molybdenum (Mo), % 0.6 to 1.4
0
Nickel (Ni), % 2.0 to 4.0
1.6 to 2.2
Nitrogen (N), % 0.14 to 0.24
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 0.8
0
Sulfur (S), % 0 to 0.0050
0 to 0.050