S82031 Stainless Steel vs. EN 1.3553 Steel

Both S82031 stainless steel and EN 1.3553 steel are iron alloys. They have 79% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S82031 stainless steel and the bottom bar is EN 1.3553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 780
720

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 980
540
Melting Completion (Liquidus), °C 1430
1620
Melting Onset (Solidus), °C 1390
1570
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
24
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
10
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
11

Otherwise Unclassified Properties

Base Metal Price, % relative 13
24
Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 2.8
8.5
Embodied Energy, MJ/kg 39
130
Embodied Water, L/kg 150
96

Common Calculations

PREN (Pitting Resistance) 27
31
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 28
24
Strength to Weight: Bending, points 24
21
Thermal Diffusivity, mm2/s 3.9
6.4
Thermal Shock Resistance, points 22
21

Alloy Composition

Carbon (C), % 0 to 0.050
0.78 to 0.86
Chromium (Cr), % 19 to 22
3.9 to 4.3
Copper (Cu), % 0 to 1.0
0 to 0.3
Iron (Fe), % 68 to 78.3
80.7 to 83.7
Manganese (Mn), % 0 to 2.5
0 to 0.4
Molybdenum (Mo), % 0.6 to 1.4
4.7 to 5.2
Nickel (Ni), % 2.0 to 4.0
0
Nitrogen (N), % 0.14 to 0.24
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.8
0 to 0.4
Sulfur (S), % 0 to 0.0050
0 to 0.015
Tungsten (W), % 0
6.0 to 6.7
Vanadium (V), % 0
1.7 to 2.0