S82031 Stainless Steel vs. EN 1.8875 Steel

Both S82031 stainless steel and EN 1.8875 steel are iron alloys. They have 76% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S82031 stainless steel and the bottom bar is EN 1.8875 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
19
Fatigue Strength, MPa 490
340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 540
410
Tensile Strength: Ultimate (UTS), MPa 780
660
Tensile Strength: Yield (Proof), MPa 570
490

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 980
420
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
3.2
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.8
1.8
Embodied Energy, MJ/kg 39
24
Embodied Water, L/kg 150
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 280
110
Resilience: Unit (Modulus of Resilience), kJ/m3 820
650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
23
Strength to Weight: Bending, points 24
21
Thermal Diffusivity, mm2/s 3.9
10
Thermal Shock Resistance, points 22
19

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.050
0 to 0.18
Chromium (Cr), % 19 to 22
0 to 1.0
Copper (Cu), % 0 to 1.0
0 to 0.3
Iron (Fe), % 68 to 78.3
93.6 to 100
Manganese (Mn), % 0 to 2.5
0 to 1.7
Molybdenum (Mo), % 0.6 to 1.4
0 to 0.7
Nickel (Ni), % 2.0 to 4.0
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.14 to 0.24
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 0.8
0 to 0.6
Sulfur (S), % 0 to 0.0050
0 to 0.0080
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15