S82441 Stainless Steel vs. EN 1.0487 Steel

Both S82441 stainless steel and EN 1.0487 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S82441 stainless steel and the bottom bar is EN 1.0487 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
27
Fatigue Strength, MPa 400
210
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 490
280
Tensile Strength: Ultimate (UTS), MPa 760
440
Tensile Strength: Yield (Proof), MPa 550
280

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1090
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.3
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
1.5
Embodied Energy, MJ/kg 45
20
Embodied Water, L/kg 170
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
100
Resilience: Unit (Modulus of Resilience), kJ/m3 740
200
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
15
Strength to Weight: Bending, points 24
16
Thermal Diffusivity, mm2/s 3.9
13
Thermal Shock Resistance, points 21
14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.030
0 to 0.16
Chromium (Cr), % 23 to 25
0 to 0.3
Copper (Cu), % 0.1 to 0.8
0 to 0.3
Iron (Fe), % 62.6 to 70.2
96.6 to 99.38
Manganese (Mn), % 2.5 to 4.0
0.6 to 1.5
Molybdenum (Mo), % 1.0 to 2.0
0 to 0.080
Nickel (Ni), % 3.0 to 4.5
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.2 to 0.3
0 to 0.012
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.4
Sulfur (S), % 0 to 0.0050
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.050