S82441 Stainless Steel vs. SAE-AISI S6 Steel

Both S82441 stainless steel and SAE-AISI S6 steel are iron alloys. They have 70% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S82441 stainless steel and the bottom bar is SAE-AISI S6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 760
670 to 1920

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1380
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
41
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 16
3.2
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.2
2.3
Embodied Energy, MJ/kg 45
33
Embodied Water, L/kg 170
56

Common Calculations

PREN (Pitting Resistance) 33
2.7
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
24 to 70
Strength to Weight: Bending, points 24
22 to 45
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 21
22 to 64

Alloy Composition

Carbon (C), % 0 to 0.030
0.4 to 0.5
Chromium (Cr), % 23 to 25
1.2 to 1.5
Copper (Cu), % 0.1 to 0.8
0 to 0.25
Iron (Fe), % 62.6 to 70.2
92.8 to 94.7
Manganese (Mn), % 2.5 to 4.0
1.2 to 1.5
Molybdenum (Mo), % 1.0 to 2.0
0.3 to 0.5
Nickel (Ni), % 3.0 to 4.5
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 0.7
2.0 to 2.5
Sulfur (S), % 0 to 0.0050
0 to 0.030
Vanadium (V), % 0
0.2 to 0.4