Z21210 Zinc vs. ASTM A217 Cast Steel
Z21210 zinc belongs to the zinc alloys classification, while ASTM A217 cast steel belongs to the iron alloys. There are 12 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is ASTM A217 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Tensile Strength: Ultimate (UTS), MPa | 150 to 170 | |
| 540 to 710 |
Thermal Properties
| Melting Completion (Liquidus), °C | 420 | |
| 1450 to 1460 |
| Melting Onset (Solidus), °C | 420 | |
| 1410 to 1420 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 26 to 50 |
| Thermal Expansion, µm/m-K | 32 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 7.3 to 9.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 35 | |
| 8.4 to 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.1 | |
| 7.8 |
Common Calculations
| Strength to Weight: Axial, points | 5.7 to 6.4 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 8.6 to 9.4 | |
| 19 to 23 |
| Thermal Diffusivity, mm2/s | 38 | |
| 6.9 to 14 |