Z21210 Zinc vs. ASTM B780 Alloy
Z21210 zinc belongs to the zinc alloys classification, while ASTM B780 alloy belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is ASTM B780 alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 70 to 76 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 35 | |
| 62 to 68 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 270 |
| Strength to Weight: Axial, points | 5.7 to 6.4 | |
| 9.1 to 16 |
| Strength to Weight: Bending, points | 8.6 to 9.4 | |
| 11 to 15 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 170 | |
| 330 to 590 |
| Thermal Expansion, µm/m-K | 32 | |
| 18 |