Z21210 Zinc vs. EN AC-44200 Aluminum

Z21210 zinc belongs to the zinc alloys classification, while EN AC-44200 aluminum belongs to the aluminum alloys. There are 12 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is Z21210 zinc and the bottom bar is EN AC-44200 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Tensile Strength: Ultimate (UTS), MPa 150 to 170
180

Thermal Properties

Melting Completion (Liquidus), °C 420
590
Melting Onset (Solidus), °C 420
580
Specific Heat Capacity, J/kg-K 400
910
Thermal Conductivity, W/m-K 110
130
Thermal Expansion, µm/m-K 32
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
35
Electrical Conductivity: Equal Weight (Specific), % IACS 35
130

Otherwise Unclassified Properties

Density, g/cm3 7.1
2.5

Common Calculations

Strength to Weight: Axial, points 5.7 to 6.4
20
Strength to Weight: Bending, points 8.6 to 9.4
28
Thermal Diffusivity, mm2/s 38
59