Z21210 Zinc vs. Nickel 725
Z21210 zinc belongs to the zinc alloys classification, while nickel 725 belongs to the nickel alloys. There are 10 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is nickel 725.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 8.5 |
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 35 | |
| 1.6 |
| Melting Completion (Liquidus), °C | 420 | |
| 1340 |
| Melting Onset (Solidus), °C | 420 | |
| 1270 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 440 |
| Strength to Weight: Axial, points | 5.7 to 6.4 | |
| 28 |
| Strength to Weight: Bending, points | 8.6 to 9.4 | |
| 24 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 170 | |
| 860 |
| Thermal Expansion, µm/m-K | 32 | |
| 13 |