Z21210 Zinc vs. C66100 Bronze
Z21210 zinc belongs to the zinc alloys classification, while C66100 bronze belongs to the copper alloys. There are 10 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is C66100 bronze.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 8.7 |
| Melting Completion (Liquidus), °C | 420 | |
| 1050 |
| Melting Onset (Solidus), °C | 420 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 400 |
| Strength to Weight: Axial, points | 5.7 to 6.4 | |
| 13 to 25 |
| Strength to Weight: Bending, points | 8.6 to 9.4 | |
| 14 to 22 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 170 | |
| 410 to 790 |
| Thermal Conductivity, W/m-K | 110 | |
| 34 |
| Thermal Diffusivity, mm2/s | 38 | |
| 9.7 |
| Thermal Expansion, µm/m-K | 32 | |
| 17 |