Z21210 Zinc vs. C99700 Brass
Z21210 zinc belongs to the zinc alloys classification, while C99700 brass belongs to the copper alloys. There are 10 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is C99700 brass.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 8.1 |
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 3.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 35 | |
| 3.3 |
| Melting Completion (Liquidus), °C | 420 | |
| 900 |
| Melting Onset (Solidus), °C | 420 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 410 |
| Strength to Weight: Axial, points | 5.7 to 6.4 | |
| 13 |
| Strength to Weight: Bending, points | 8.6 to 9.4 | |
| 14 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 170 | |
| 380 |
| Thermal Expansion, µm/m-K | 32 | |
| 20 |