Z21210 Zinc vs. K93050 Alloy
Z21210 zinc belongs to the zinc alloys classification, while K93050 alloy belongs to the iron alloys. There are 8 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is K93050 alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 8.2 |
| Melting Completion (Liquidus), °C | 420 | |
| 1430 |
| Melting Onset (Solidus), °C | 420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 460 |
| Strength to Weight: Axial, points | 5.7 to 6.4 | |
| 17 to 23 |
| Strength to Weight: Bending, points | 8.6 to 9.4 | |
| 17 to 21 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 170 | |
| 500 to 680 |
| Thermal Expansion, µm/m-K | 32 | |
| 12 |