Yttria vs. Marble

Yttria belongs to the oxide-based engineering ceramics classification, while marble belongs to the natural stone. There are 10 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is yttria and the bottom bar is marble.

Yttria (Yttrium Oxide, Y₂O₃)Marble

Metric UnitsUS Customary Units

Material Properties

Compressive (Crushing) Strength, MPa		390
Compressive (Crushing) Strength, MPa		540

Density, g/cm³		5.0
Density, g/cm³		2.7

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		54

Maximum Temperature: Mechanical, °C		2000
Maximum Temperature: Mechanical, °C		250

Specific Heat Capacity, J/kg-K		440
Specific Heat Capacity, J/kg-K		870

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		11

Stiffness to Weight: Bending, points		32
Stiffness to Weight: Bending, points		47

Thermal Conductivity, W/m-K		0.3
Thermal Conductivity, W/m-K		3.1

Thermal Diffusivity, mm²/s		0.14
Thermal Diffusivity, mm²/s		1.3

Thermal Expansion, µm/m-K		8.0
Thermal Expansion, µm/m-K		21