ZC63A Magnesium vs. Z24311 Zinc
ZC63A magnesium belongs to the magnesium alloys classification, while Z24311 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ZC63A magnesium and the bottom bar is Z24311 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 48 | |
| 87 |
| Elongation at Break, % | 3.3 | |
| 63 |
| Poisson's Ratio | 0.29 | |
| 0.25 |
| Shear Modulus, GPa | 19 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 220 | |
| 140 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 98 | |
| 90 |
| Melting Completion (Liquidus), °C | 550 | |
| 410 |
| Melting Onset (Solidus), °C | 470 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 950 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 110 |
| Thermal Expansion, µm/m-K | 26 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 11 |
| Density, g/cm3 | 2.1 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 22 | |
| 2.8 |
| Embodied Energy, MJ/kg | 150 | |
| 53 |
| Embodied Water, L/kg | 920 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.3 | |
| 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
| 81 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 58 | |
| 23 |
| Strength to Weight: Axial, points | 29 | |
| 6.1 |
| Strength to Weight: Bending, points | 38 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 58 | |
| 44 |
| Thermal Shock Resistance, points | 12 | |
| 4.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0020 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 2.4 to 3.0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0.030 to 0.080 |
| Magnesium (Mg), % | 89.2 to 91.9 | |
| 0 to 0.0015 |
| Manganese (Mn), % | 0.25 to 0.75 | |
| 0 to 0.015 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Zinc (Zn), % | 5.5 to 6.5 | |
| 99.862 to 100 |
| Residuals, % | 0 to 0.3 | |
| 0 |