ZE41A Magnesium vs. SAE-AISI 1527 Steel
ZE41A magnesium belongs to the magnesium alloys classification, while SAE-AISI 1527 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ZE41A magnesium and the bottom bar is SAE-AISI 1527 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 63 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 190 |
| Elongation at Break, % | 3.3 | |
| 13 to 21 |
| Fatigue Strength, MPa | 98 | |
| 220 to 350 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 18 | |
| 73 |
| Shear Strength, MPa | 150 | |
| 370 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 590 to 640 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 320 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 400 |
| Melting Completion (Liquidus), °C | 640 | |
| 1460 |
| Melting Onset (Solidus), °C | 540 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 52 |
| Thermal Expansion, µm/m-K | 27 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 1.8 |
| Density, g/cm3 | 1.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 1.4 |
| Embodied Energy, MJ/kg | 170 | |
| 19 |
| Embodied Water, L/kg | 940 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.1 | |
| 82 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 260 to 800 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 63 | |
| 24 |
| Strength to Weight: Axial, points | 31 | |
| 21 to 23 |
| Strength to Weight: Bending, points | 41 | |
| 20 to 21 |
| Thermal Diffusivity, mm2/s | 59 | |
| 14 |
| Thermal Shock Resistance, points | 12 | |
| 19 to 20 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.22 to 0.29 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 | |
| 98.1 to 98.6 |
| Magnesium (Mg), % | 91.7 to 95.4 | |
| 0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 1.2 to 1.5 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Unspecified Rare Earths, % | 0.75 to 1.8 | |
| 0 |
| Zinc (Zn), % | 3.5 to 5.0 | |
| 0 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |