ZK60A Magnesium vs. 92-silver 8-tin-oxide
ZK60A magnesium belongs to the magnesium alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is ZK60A magnesium and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 to 30 | |
| 76 to 80 |
| Elongation at Break, % | 4.5 to 9.9 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 29 | |
| 62 to 110 |
| Shear Strength, MPa | 170 to 190 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 330 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 120 to 300 |