Zamak 3 vs. Grade Ti-Pd16 Titanium
Zamak 3 belongs to the zinc alloys classification, while grade Ti-Pd16 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is Zamak 3 and the bottom bar is grade Ti-Pd16 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 83 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 86 | |
| 110 |
| Elongation at Break, % | 11 | |
| 17 |
| Fatigue Strength, MPa | 48 | |
| 200 |
| Poisson's Ratio | 0.25 | |
| 0.32 |
| Rockwell B Hardness | 50 | |
| 83 |
| Shear Modulus, GPa | 33 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 95 | |
| 320 |
| Melting Completion (Liquidus), °C | 390 | |
| 1660 |
| Melting Onset (Solidus), °C | 380 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 540 |
| Thermal Conductivity, W/m-K | 110 | |
| 22 |
| Thermal Expansion, µm/m-K | 27 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 38 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.4 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 36 |
| Embodied Energy, MJ/kg | 57 | |
| 600 |
| Embodied Water, L/kg | 380 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 | |
| 62 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 440 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 35 |
| Strength to Weight: Axial, points | 12 | |
| 24 |
| Strength to Weight: Bending, points | 15 | |
| 26 |
| Thermal Diffusivity, mm2/s | 43 | |
| 8.9 |
| Thermal Shock Resistance, points | 8.6 | |
| 30 |
Alloy Composition
| Aluminum (Al), % | 3.5 to 4.3 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.0050 | |
| 0 |
| Magnesium (Mg), % | 0.020 to 0.060 | |
| 0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Silicon (Si), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.8 to 99.96 |
| Zinc (Zn), % | 95.3 to 96.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |