Zamak 7 vs. C82400 Copper
Zamak 7 belongs to the zinc alloys classification, while C82400 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Zamak 7 and the bottom bar is C82400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 86 | |
| 120 |
| Elongation at Break, % | 13 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.25 | |
| 0.33 |
| Shear Modulus, GPa | 33 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 500 to 1030 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 260 to 970 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 95 | |
| 270 |
| Melting Completion (Liquidus), °C | 390 | |
| 1000 |
| Melting Onset (Solidus), °C | 380 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 130 |
| Thermal Expansion, µm/m-K | 27 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 38 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.4 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 8.9 |
| Embodied Energy, MJ/kg | 57 | |
| 140 |
| Embodied Water, L/kg | 380 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 | |
| 10 to 83 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 270 to 3870 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 12 | |
| 16 to 33 |
| Strength to Weight: Bending, points | 15 | |
| 16 to 26 |
| Thermal Diffusivity, mm2/s | 43 | |
| 39 |
| Thermal Shock Resistance, points | 8.6 | |
| 17 to 36 |
Alloy Composition
| Aluminum (Al), % | 3.5 to 4.3 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 1.6 to 1.9 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.2 to 0.65 |
| Copper (Cu), % | 0 to 0.25 | |
| 96 to 98.2 |
| Iron (Fe), % | 0 to 0.075 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.0030 | |
| 0 to 0.020 |
| Magnesium (Mg), % | 0.0050 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0.0050 to 0.020 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 to 0.0010 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.12 |
| Zinc (Zn), % | 95.3 to 96.5 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |