ZA-27 vs. 5154A Aluminum
ZA-27 belongs to the zinc alloys classification, while 5154A aluminum belongs to the aluminum alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ZA-27 and the bottom bar is 5154A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 100 to 120 | |
| 58 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 68 |
| Elongation at Break, % | 2.0 to 4.5 | |
| 1.1 to 19 |
| Fatigue Strength, MPa | 110 to 170 | |
| 83 to 160 |
| Poisson's Ratio | 0.27 | |
| 0.33 |
| Shear Modulus, GPa | 31 | |
| 26 |
| Shear Strength, MPa | 230 to 330 | |
| 140 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 430 | |
| 230 to 370 |
| Tensile Strength: Yield (Proof), MPa | 260 to 370 | |
| 96 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 190 |
| Melting Completion (Liquidus), °C | 480 | |
| 650 |
| Melting Onset (Solidus), °C | 380 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 530 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 26 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 53 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 5.0 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 8.8 |
| Embodied Energy, MJ/kg | 80 | |
| 150 |
| Embodied Water, L/kg | 570 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 to 18 | |
| 4.0 to 36 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 to 890 | |
| 68 to 760 |
| Stiffness to Weight: Axial, points | 8.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 28 | |
| 51 |
| Strength to Weight: Axial, points | 22 to 24 | |
| 24 to 38 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 31 to 43 |
| Thermal Diffusivity, mm2/s | 47 | |
| 53 |
| Thermal Shock Resistance, points | 14 to 15 | |
| 10 to 16 |
Alloy Composition
| Aluminum (Al), % | 25 to 28 | |
| 93.7 to 96.9 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 2.0 to 2.5 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 |
| Magnesium (Mg), % | 0.010 to 0.020 | |
| 3.1 to 3.9 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.5 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 69.3 to 73 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |