ZA-27 belongs to the zinc alloys classification, while 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (30, in this case) are not shown.
For each property being compared, the top bar is ZA-27 and the bottom bar is 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 77 to 82 |
| Elongation at Break, % | 2.0 to 4.5 | |
| 7.0 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 to 18 | |
| 20 to 68 |
| Shear Strength, MPa | 230 to 330 | |
| 160 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 430 | |
| 230 to 300 |
| Tensile Strength: Yield (Proof), MPa | 260 to 370 | |
| 120 to 280 |