ZA-27 vs. EN 1.4857 Stainless Steel

ZA-27 belongs to the zinc alloys classification, while EN 1.4857 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ZA-27 and the bottom bar is EN 1.4857 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 120
150
Elastic (Young's, Tensile) Modulus, GPa 78
200
Elongation at Break, % 2.0 to 4.5
6.7
Fatigue Strength, MPa 110 to 170
120
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 31
78
Tensile Strength: Ultimate (UTS), MPa 400 to 430
500
Tensile Strength: Yield (Proof), MPa 260 to 370
250

Thermal Properties

Latent Heat of Fusion, J/g 130
330
Maximum Temperature: Mechanical, °C 120
1100
Melting Completion (Liquidus), °C 480
1370
Melting Onset (Solidus), °C 380
1320
Specific Heat Capacity, J/kg-K 530
480
Thermal Conductivity, W/m-K 130
13
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 53
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 11
34
Density, g/cm3 5.0
7.9
Embodied Carbon, kg CO2/kg material 4.2
5.7
Embodied Energy, MJ/kg 80
81
Embodied Water, L/kg 570
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 8.1 to 18
28
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 890
150
Stiffness to Weight: Axial, points 8.6
14
Stiffness to Weight: Bending, points 28
25
Strength to Weight: Axial, points 22 to 24
18
Strength to Weight: Bending, points 24 to 25
18
Thermal Diffusivity, mm2/s 47
3.4
Thermal Shock Resistance, points 14 to 15
11

Alloy Composition

Aluminum (Al), % 25 to 28
0
Cadmium (Cd), % 0 to 0.0060
0
Carbon (C), % 0
0.3 to 0.5
Chromium (Cr), % 0
24 to 27
Copper (Cu), % 2.0 to 2.5
0
Iron (Fe), % 0 to 0.1
31.4 to 41.7
Lead (Pb), % 0 to 0.0060
0
Magnesium (Mg), % 0.010 to 0.020
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.020
33 to 36
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.080
1.0 to 2.5
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 69.3 to 73
0