ZA-27 vs. EN 1.7711 Steel
ZA-27 belongs to the zinc alloys classification, while EN 1.7711 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ZA-27 and the bottom bar is EN 1.7711 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 100 to 120 | |
| 210 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 190 |
| Elongation at Break, % | 2.0 to 4.5 | |
| 16 to 22 |
| Fatigue Strength, MPa | 110 to 170 | |
| 290 to 520 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 31 | |
| 73 |
| Shear Strength, MPa | 230 to 330 | |
| 440 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 430 | |
| 690 to 930 |
| Tensile Strength: Yield (Proof), MPa | 260 to 370 | |
| 400 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 430 |
| Melting Completion (Liquidus), °C | 480 | |
| 1460 |
| Melting Onset (Solidus), °C | 380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 530 | |
| 470 |
| Thermal Conductivity, W/m-K | 130 | |
| 33 |
| Thermal Expansion, µm/m-K | 26 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 53 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 3.0 |
| Density, g/cm3 | 5.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 2.3 |
| Embodied Energy, MJ/kg | 80 | |
| 32 |
| Embodied Water, L/kg | 570 | |
| 54 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 to 18 | |
| 130 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 to 890 | |
| 430 to 1690 |
| Stiffness to Weight: Axial, points | 8.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 28 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 24 | |
| 24 to 33 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 22 to 27 |
| Thermal Diffusivity, mm2/s | 47 | |
| 8.9 |
| Thermal Shock Resistance, points | 14 to 15 | |
| 24 to 32 |
Alloy Composition
| Aluminum (Al), % | 25 to 28 | |
| 0 to 0.015 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.36 to 0.44 |
| Chromium (Cr), % | 0 | |
| 0.9 to 1.2 |
| Copper (Cu), % | 2.0 to 2.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 96 to 97.5 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 |
| Magnesium (Mg), % | 0.010 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.45 to 0.85 |
| Molybdenum (Mo), % | 0 | |
| 0.5 to 0.65 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |
| Zinc (Zn), % | 69.3 to 73 | |
| 0 |