ZA-27 vs. Grade 300 Maraging Steel
ZA-27 belongs to the zinc alloys classification, while grade 300 maraging steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ZA-27 and the bottom bar is grade 300 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 260 to 370 | |
| 730 to 1880 |
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 190 |
| Elongation at Break, % | 2.0 to 4.5 | |
| 6.5 to 18 |
| Poisson's Ratio | 0.27 | |
| 0.3 |
| Shear Modulus, GPa | 31 | |
| 75 |
| Shear Strength, MPa | 230 to 330 | |
| 640 to 1190 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 430 | |
| 1030 to 2030 |
| Tensile Strength: Yield (Proof), MPa | 260 to 370 | |
| 760 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 270 |
| Melting Completion (Liquidus), °C | 480 | |
| 1480 |
| Melting Onset (Solidus), °C | 380 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 530 | |
| 450 |
| Thermal Expansion, µm/m-K | 26 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 34 |
| Density, g/cm3 | 5.0 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 5.1 |
| Embodied Energy, MJ/kg | 80 | |
| 68 |
| Embodied Water, L/kg | 570 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 to 18 | |
| 130 to 170 |
| Stiffness to Weight: Axial, points | 8.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 28 | |
| 23 |
| Strength to Weight: Axial, points | 22 to 24 | |
| 35 to 68 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 28 to 43 |
| Thermal Shock Resistance, points | 14 to 15 | |
| 31 to 62 |
Alloy Composition
| Aluminum (Al), % | 25 to 28 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 8.5 to 9.5 |
| Copper (Cu), % | 2.0 to 2.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 65 to 68.4 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 |
| Magnesium (Mg), % | 0.010 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 0 to 0.020 | |
| 18 to 19 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.5 to 0.8 |
| Zinc (Zn), % | 69.3 to 73 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |