ZA-8 vs. N07041 Nickel
ZA-8 belongs to the zinc alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is ZA-8 and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 85 to 86 | |
| 220 |
| Elongation at Break, % | 1.3 to 8.0 | |
| 14 |
| Fatigue Strength, MPa | 51 to 100 | |
| 540 |
| Shear Strength, MPa | 240 to 280 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 370 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 210 to 290 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 380 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 120 | |
| 11 |
| Thermal Expansion, µm/m-K | 23 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.3 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.8 to 28 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 490 | |
| 2510 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 15 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 9.3 to 17 | |
| 47 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 34 |
| Thermal Diffusivity, mm2/s | 42 | |
| 3.0 |
| Thermal Shock Resistance, points | 7.6 to 13 | |
| 38 |