Z41321 Zinc vs. EN 1.3549 Stainless Steel
Z41321 zinc belongs to the zinc alloys classification, while EN 1.3549 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is Z41321 zinc and the bottom bar is EN 1.3549 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 200 |
| Poisson's Ratio | 0.25 | |
| 0.28 |
| Shear Modulus, GPa | 35 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 910 |
| Melting Completion (Liquidus), °C | 410 | |
| 1430 |
| Melting Onset (Solidus), °C | 400 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 110 | |
| 21 |
| Thermal Expansion, µm/m-K | 26 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 10 |
| Density, g/cm3 | 6.6 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 54 | |
| 37 |
| Embodied Water, L/kg | 340 | |
| 130 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 7.9 | |
| 27 |
| Strength to Weight: Bending, points | 11 | |
| 24 |
| Thermal Diffusivity, mm2/s | 44 | |
| 5.6 |
| Thermal Shock Resistance, points | 5.9 | |
| 26 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.85 to 1.0 |
| Chromium (Cr), % | 0 | |
| 17 to 19 |
| Copper (Cu), % | 0.5 to 1.0 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 77.5 to 82 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Titanium (Ti), % | 0.080 to 0.18 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.070 to 0.12 |
| Zinc (Zn), % | 98.8 to 99.42 | |
| 0 |