Z41321 Zinc vs. N08135 Stainless Steel

Z41321 zinc belongs to the zinc alloys classification, while N08135 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is N08135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 60
46
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
80
Tensile Strength: Ultimate (UTS), MPa 190
570
Tensile Strength: Yield (Proof), MPa 150
240

Thermal Properties

Latent Heat of Fusion, J/g 110
310
Maximum Temperature: Mechanical, °C 90
1100
Melting Completion (Liquidus), °C 410
1440
Melting Onset (Solidus), °C 400
1390
Specific Heat Capacity, J/kg-K 390
460
Thermal Expansion, µm/m-K 26
16

Otherwise Unclassified Properties

Base Metal Price, % relative 12
39
Density, g/cm3 6.6
8.2
Embodied Carbon, kg CO2/kg material 2.8
6.8
Embodied Energy, MJ/kg 54
94
Embodied Water, L/kg 340
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
210
Resilience: Unit (Modulus of Resilience), kJ/m3 130
140
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
19
Strength to Weight: Bending, points 11
19
Thermal Shock Resistance, points 5.9
13

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
20.5 to 23.5
Copper (Cu), % 0.5 to 1.0
0 to 0.7
Iron (Fe), % 0 to 0.010
30.2 to 42.3
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
33 to 38
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0
Tungsten (W), % 0
0.2 to 0.8
Zinc (Zn), % 98.8 to 99.42
0