Z40101 Zinc vs. ZA-12
Both Z40101 zinc and ZA-12 are zinc alloys. They have 88% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Z40101 zinc and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 83 |
| Elongation at Break, % | 44 | |
| 1.6 to 5.3 |
| Poisson's Ratio | 0.25 | |
| 0.26 |
| Shear Modulus, GPa | 35 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 130 | |
| 260 to 400 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 210 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 100 |
| Melting Completion (Liquidus), °C | 410 | |
| 430 |
| Melting Onset (Solidus), °C | 400 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 26 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 11 |
| Density, g/cm3 | 6.6 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.4 |
| Embodied Energy, MJ/kg | 53 | |
| 64 |
| Embodied Water, L/kg | 340 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 4.0 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 | |
| 260 to 620 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 5.7 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 8.9 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 44 | |
| 43 |
| Thermal Shock Resistance, points | 4.2 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 to 0.0060 |
| Copper (Cu), % | 0.080 to 0.4 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.060 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 99.542 to 99.92 | |
| 87.1 to 89 |