Z41121 zinc belongs to the zinc alloys classification, while AWS BVAg-0 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is Z41121 zinc and the bottom bar is AWS BVAg-0.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
71
Poisson's Ratio 0.25
0.37
Shear Modulus, GPa 35
26
Tensile Strength: Ultimate (UTS), MPa 140
130

Thermal Properties

Latent Heat of Fusion, J/g 110
110
Melting Completion (Liquidus), °C 410
960
Melting Onset (Solidus), °C 400
960
Specific Heat Capacity, J/kg-K 390
240
Thermal Expansion, µm/m-K 26
20

Otherwise Unclassified Properties

Density, g/cm3 6.6
10

Common Calculations

Stiffness to Weight: Axial, points 7.4
3.8
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 6.1
3.4
Strength to Weight: Bending, points 9.3
5.4
Thermal Shock Resistance, points 4.6
6.6

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0 to 0.0010
Carbon (C), % 0
0 to 0.0050
Copper (Cu), % 0.080 to 0.49
0 to 0.050
Iron (Fe), % 0 to 0.010
0
Lead (Pb), % 0 to 0.010
0 to 0.0020
Phosphorus (P), % 0
0 to 0.0020
Silver (Ag), % 0
99.95 to 100
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.050 to 0.18
0
Zinc (Zn), % 99.292 to 99.87
0 to 0.0010