Z41121 Zinc vs. Grade 360 Molybdenum

Z41121 zinc belongs to the zinc alloys classification, while grade 360 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is Z41121 zinc and the bottom bar is grade 360 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
310
Elongation at Break, % 50
6.3 to 17
Poisson's Ratio 0.25
0.31
Shear Modulus, GPa 35
120
Tensile Strength: Ultimate (UTS), MPa 140
430 to 620
Tensile Strength: Yield (Proof), MPa 120
270 to 530

Thermal Properties

Latent Heat of Fusion, J/g 110
370
Specific Heat Capacity, J/kg-K 390
250
Thermal Expansion, µm/m-K 26
7.0

Otherwise Unclassified Properties

Density, g/cm3 6.6
10
Embodied Carbon, kg CO2/kg material 2.8
28
Embodied Energy, MJ/kg 54
330
Embodied Water, L/kg 340
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 68
37 to 64
Resilience: Unit (Modulus of Resilience), kJ/m3 79
120 to 450
Stiffness to Weight: Axial, points 7.4
17
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 6.1
12 to 17
Strength to Weight: Bending, points 9.3
12 to 16
Thermal Shock Resistance, points 4.6
14 to 21

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.030
Copper (Cu), % 0.080 to 0.49
0
Iron (Fe), % 0 to 0.010
0 to 0.010
Lead (Pb), % 0 to 0.010
0
Molybdenum (Mo), % 0
99.9 to 100
Nickel (Ni), % 0
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0015
Silicon (Si), % 0
0 to 0.010
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.050 to 0.18
0
Zinc (Zn), % 99.292 to 99.87
0