Zinc Sulfide vs. Beryllia
Zinc sulfide belongs to the non-glass optical ceramics classification, while beryllia belongs to the oxide-based engineering ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is zinc sulfide and the bottom bar is beryllia.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 4.1 | |
| 2.9 |
| Elastic (Young's, Tensile) Modulus, GPa | 75 | |
| 350 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 1050 |
| Stiffness to Weight: Axial, points | 10 | |
| 67 |
| Stiffness to Weight: Bending, points | 34 | |
| 82 |
| Thermal Conductivity, W/m-K | 27 | |
| 270 |
| Thermal Diffusivity, mm2/s | 13 | |
| 89 |
| Thermal Expansion, µm/m-K | 6.5 | |
| 8.0 |