Zircon vs. Aluminum Nitride
Zircon belongs to the oxide-based engineering ceramics classification, while aluminum nitride belongs to the non-oxide engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is zircon and the bottom bar is aluminum nitride.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.9 | |
| 2.9 to 3.3 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 8.8 | |
| 6.9 to 28 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.9 | |
| 15 to 56 |
| Flexural Strength, MPa | 450 | |
| 190 to 400 |
| Maximum Temperature: Mechanical, °C | 1650 | |
| 1380 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 80 to 190 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 4.2 to 5.4 |