Zircon vs. Mullite
Both zircon and mullite are oxide-based engineering ceramics. There are 10 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is zircon and the bottom bar is mullite.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.9 | |
| 2.7 to 3.0 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 8.8 | |
| 6.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.9 | |
| 16 to 17 |
| Flexural Strength, MPa | 450 | |
| 130 to 160 |
| Maximum Temperature: Mechanical, °C | 1650 | |
| 1680 |
| Strength to Weight: Axial, points | 21 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 25 | |
| 22 to 24 |
| Tensile Strength: Ultimate (UTS), MPa | 290 | |
| 160 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 3.5 to 11 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 5.8 |