Zirconia vs. Silver Chloride
Zirconia belongs to the oxide-based engineering ceramics classification, while silver chloride belongs to the non-glass optical ceramics. There are 10 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is zirconia and the bottom bar is silver chloride.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 5.7 to 6.0 | |
| 5.6 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 28 | |
| 12 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 to 200 | |
| 20 |
| Poisson's Ratio | 0.25 to 0.29 | |
| 0.4 |
| Specific Heat Capacity, J/kg-K | 400 to 510 | |
| 360 |
| Stiffness to Weight: Axial, points | 19 | |
| 2.0 |
| Stiffness to Weight: Bending, points | 33 to 34 | |
| 16 |
| Thermal Conductivity, W/m-K | 2.2 to 4.3 | |
| 1.2 |
| Thermal Diffusivity, mm2/s | 0.73 to 1.8 | |
| 0.57 |
| Thermal Expansion, µm/m-K | 8.8 to 9.5 | |
| 31 |