Zirconia vs. Thallium Bromoiodide
Zirconia belongs to the oxide-based engineering ceramics classification, while thallium bromoiodide belongs to the non-glass optical ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is zirconia and the bottom bar is thallium bromoiodide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 5.7 to 6.0 | |
| 7.4 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 to 200 | |
| 31 |
| Poisson's Ratio | 0.25 to 0.29 | |
| 0.37 |
| Specific Heat Capacity, J/kg-K | 400 to 510 | |
| 150 |
| Stiffness to Weight: Axial, points | 19 | |
| 2.3 |
| Stiffness to Weight: Bending, points | 33 to 34 | |
| 14 |
| Thermal Conductivity, W/m-K | 2.2 to 4.3 | |
| 0.55 |
| Thermal Diffusivity, mm2/s | 0.73 to 1.8 | |
| 0.5 |
| Thermal Expansion, µm/m-K | 8.8 to 9.5 | |
| 6.0 |