Zirconia vs. C-310 Titania-based Ceramic
Both zirconia and C-310 titania-based ceramic are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is zirconia and the bottom bar is C-310 titania-based ceramic.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 5.7 to 6.0 | |
| 3.7 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.7 to 9.0 | |
| 9.0 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 4.5 to 11 | |
| 10 |
| Flexural Strength, MPa | 630 to 970 | |
| 75 |
| Specific Heat Capacity, J/kg-K | 400 to 510 | |
| 750 |
| Thermal Conductivity, W/m-K | 2.2 to 4.3 | |
| 3.5 |
| Thermal Diffusivity, mm2/s | 0.73 to 1.8 | |
| 1.3 |
| Thermal Expansion, µm/m-K | 8.8 to 9.5 | |
| 7.0 |