1100-H16 Aluminum
1100-H16 aluminum is 1100 aluminum in the H16 temper. To achieve this temper, the metal is strain hardened to a strength that is roughly 3/4 of the way between annealed (O) and full-hard (H18). The graph bars on the material properties cards below compare 1100-H16 aluminum to: 1000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
38
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
6.0 %
Fatigue Strength
61 MPa 8.8 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
84 MPa 12 x 103 psi
Tensile Strength: Ultimate (UTS)
150 MPa 21 x 103 psi
Tensile Strength: Yield (Proof)
130 MPa 19 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
660 °C 1210 °F
Melting Onset (Solidus)
640 °C 1190 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
220 W/m-K 130 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
59 % IACS
Electrical Conductivity: Equal Weight (Specific)
190 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.0 % relative
Calomel Potential
-740 mV
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.2 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
8.5 MJ/m3
Resilience: Unit (Modulus of Resilience)
130 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
15 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
90 mm2/s
Thermal Shock Resistance
6.4 points
Alloy Composition
| Al | 99 to 99.95 | |
| Si | 0 to 1.0 | |
| Fe | 0 to 1.0 | |
| Cu | 0.050 to 0.2 | |
| Zn | 0 to 0.1 | |
| Mn | 0 to 0.050 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes
ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube
Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014.
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
Aluminum Standards and Data, Aluminum Association Inc., 2013
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993