2017-T4 Aluminum
2017-T4 aluminum is 2017 aluminum in the T4 temper. To achieve this temper, the metal is solution heat-treated and naturally aged. It has the highest ductility compared to the other variants of 2017 aluminum.
The graph bars on the material properties cards below compare 2017-T4 aluminum to: 2000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
110
Elastic (Young's, Tensile) Modulus
71 GPa 10 x 106 psi
Elongation at Break
18 %
Fatigue Strength
130 MPa 18 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
27 GPa 3.9 x 106 psi
Shear Strength
260 MPa 38 x 103 psi
Tensile Strength: Ultimate (UTS)
420 MPa 61 x 103 psi
Tensile Strength: Yield (Proof)
260 MPa 37 x 103 psi
Thermal Properties
Latent Heat of Fusion
390 J/g
Maximum Temperature: Mechanical
190 °C 380 °F
Melting Completion (Liquidus)
640 °C 1180 °F
Melting Onset (Solidus)
510 °C 950 °F
Specific Heat Capacity
880 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
150 W/m-K 86 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
38 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
10 % relative
Density
3.0 g/cm3 190 lb/ft3
Embodied Carbon
8.0 kg CO2/kg material
Embodied Energy
150 MJ/kg 64 x 103 BTU/lb
Embodied Water
1140 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
66 MJ/m3
Resilience: Unit (Modulus of Resilience)
470 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
46 points
Strength to Weight: Axial
39 points
Strength to Weight: Bending
42 points
Thermal Diffusivity
56 mm2/s
Thermal Shock Resistance
18 points
Alloy Composition
| Al | 91.6 to 95.5 | |
| Cu | 3.5 to 4.5 | |
| Mn | 0.4 to 1.0 | |
| Mg | 0.4 to 0.8 | |
| Si | 0.2 to 0.8 | |
| Fe | 0 to 0.7 | |
| Zn | 0 to 0.25 | |
| Ti | 0 to 0.15 | |
| Cr | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
Aerospace Materials, Brian Cantor et al. (editors), 2001
Aluminum Standards and Data, Aluminum Association Inc., 2013
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993